The mixture is intended for the arrangement of a leveling layer with a grade of strength not less than M160 on mineral surfaces (concrete, cement-sand screed) inside rooms with dry and wet operation, with a layer of not less than 3 mm. It can be used when arranging a heated floor with water and electric heating for pouring heating elements. When arranging floating screeds as part of thermal insulation systems, the layer thickness must be at least 40 mm. Suitable for application by plastering stations.
| Proportions of water for mixing, l/25 kg | 4.0-4.5 |
| Recommended thickness of the leveling layer, mm | 3 ... 100 |
| Consumption per 1 mm layer, kg/m² | 1,8 |
| Coverage area from 1 bag of 25 kg of dry mix (layer thickness 3 mm), m² | 4,6 |
| Shelf life of the mortar mixture, min, not less | 20 |
| Time of readiness of the leveling layer after laying: - technological passage, hours - laying of ceramic tiles, days - laying of other coatings, days |
4-6 3 7 |
| Compressive strength in 28 days, MPa, not less | 16 |
| base and ambient temperature during application, ºС | +5 ... +30 |
The mixture is intended for the arrangement of a leveling layer with a grade of strength not less than M160 on mineral surfaces (concrete, cement-sand screed) inside rooms with dry and wet operation, with a layer of not less than 3 mm. It can be used when arranging a heated floor with water and electric heating for pouring heating elements. When arranging floating screeds as part of thermal insulation systems, the layer thickness must be at least 40 mm. Suitable for application by plastering stations.
| Proportions of water for mixing, l/25 kg | 4.0-4.5 |
| Recommended thickness of the leveling layer, mm | 3 ... 100 |
| Consumption per 1 mm layer, kg/m² | 1,8 |
| Coverage area from 1 bag of 25 kg of dry mix (layer thickness 3 mm), m² | 4,6 |
| Shelf life of the mortar mixture, min, not less | 20 |
| Time of readiness of the leveling layer after laying: - technological passage, hours - laying of ceramic tiles, days - laying of other coatings, days |
4-6 3 7 |
| Compressive strength in 28 days, MPa, not less | 16 |
| base and ambient temperature during application, ºС | +5 ... +30 |