The self-leveling mixture is intended for performing a leveling layer (2…50 mm) on concrete bases, cement layers, arranging floors with water and electric heating elements for subsequent laying of linoleum, laminate, ceramic tiles and other coatings in residential, public, administrative and household premises with low intensity of exposure to liquids.
| Water consumption, per 25 kg of dry mix, l | 4.0-4.5 |
| Recommended thickness of the leveling layer, mm | 2...50 |
| Consumption per 1 mm of layer, kg/m² | 1.8 |
| Coverage area from a bag of 25 kg of dry mix (layer thickness 10 mm), m² | 1.3 |
| Storage life of the mortar mixture, min, not less than | 20 |
| Ready time after laying:
- technological passage, h - application of coatings with water-based adhesives (laying ceramic tiles, etc.), days - also (including painting, laying parquet), with organic-based adhesives - after reaching the calculated humidity and strength, but not earlier, days |
8 7 10 |
| Compressive strength limit at the age of 28 days, MPa, not less than | 16 |
| Substrate and ambient temperature during application, ºС | +5 ... +30 |
The self-leveling mixture is intended for performing a leveling layer (2…50 mm) on concrete bases, cement layers, arranging floors with water and electric heating elements for subsequent laying of linoleum, laminate, ceramic tiles and other coatings in residential, public, administrative and household premises with low intensity of exposure to liquids.
| Water consumption, per 25 kg of dry mix, l | 4.0-4.5 |
| Recommended thickness of the leveling layer, mm | 2...50 |
| Consumption per 1 mm of layer, kg/m² | 1.8 |
| Coverage area from a bag of 25 kg of dry mix (layer thickness 10 mm), m² | 1.3 |
| Storage life of the mortar mixture, min, not less than | 20 |
| Ready time after laying:
- technological passage, h - application of coatings with water-based adhesives (laying ceramic tiles, etc.), days - also (including painting, laying parquet), with organic-based adhesives - after reaching the calculated humidity and strength, but not earlier, days |
8 7 10 |
| Compressive strength limit at the age of 28 days, MPa, not less than | 16 |
| Substrate and ambient temperature during application, ºС | +5 ... +30 |