POLIMIN SB-10 decorative plaster is intended for protection and decoration of strong cement-lime, lime and gypsum plasters, prepared concrete, brick and other mineral surfaces, insulation systems. It is used for finishing the facades of residential, commercial, industrial, warehouse and other buildings, as well as for creating a decorative textured coating “”GRAINY TEXTURE””. It has a uniform medium-grained texture. It is intended for tinting. It is tinted according to the catalogs: Monicolor, RAL, NCS, Spirit. Base A – white, tinted only in light and pastel colors. Base C – transparent, only for tinting in dark and saturated colors. The name of the Base (A/C) is indicated on the packaging.
| Color | white/for tinting |
| Appearance of the coating after drying | "GRAINY TEXTURE" |
| Term of formation of the surface film, min | 15 |
| Adhesion strength to the base, not less than, MPa | 0,5 |
| Drying time, h | 24 |
| Water permeability, not more than, kg/m² h | 0,2 |
| *Maximum plastering area from one bucket 25 kg, up to, m² | 10 |
| Density, kg/L | 1,75 - 1,95 |
| Consumption, kg/m² | 2,5 - 2,7 |
| Particle size, mm up to | 1.5 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
POLIMIN SB-10 decorative plaster is intended for protection and decoration of strong cement-lime, lime and gypsum plasters, prepared concrete, brick and other mineral surfaces, insulation systems. It is used for finishing the facades of residential, commercial, industrial, warehouse and other buildings, as well as for creating a decorative textured coating “”GRAINY TEXTURE””. It has a uniform medium-grained texture. It is intended for tinting. It is tinted according to the catalogs: Monicolor, RAL, NCS, Spirit. Base A – white, tinted only in light and pastel colors. Base C – transparent, only for tinting in dark and saturated colors. The name of the Base (A/C) is indicated on the packaging.
| Color | white/for tinting |
| Appearance of the coating after drying | "GRAINY TEXTURE" |
| Term of formation of the surface film, min | 15 |
| Adhesion strength to the base, not less than, MPa | 0,5 |
| Drying time, h | 24 |
| Water permeability, not more than, kg/m² h | 0,2 |
| *Maximum plastering area from one bucket 25 kg, up to, m² | 10 |
| Density, kg/L | 1,75 - 1,95 |
| Consumption, kg/m² | 2,5 - 2,7 |
| Particle size, mm up to | 1.5 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |