It is used for high-quality plastering work on various mineral surfaces (concrete, brick) indoors and outdoors for plastering walls that are protected from moisture. Recommended for both mechanized and manual application. After hardening, it is a strong base for gypsum and lime putties and interior decorative plasters.
Thanks to the improved formula, the material provides:
• resistance to mold and fungi
• resistance to slipping due to good thixotropic properties
• machine and manual application
• high vapor permeability and crack resistance.
| Water consumption, per 30 kg of dry mix, l | 4,8...5,8 |
| Dry mix consumption per 1 mm of layer, kg/m², from | 1,3 |
| Estimated plaster layer thickness, mm, up to | 25 |
| Storage shelf life, h, not less than | 1 |
| Adhesion strength to the base in air-dry conditions, MPa, not less than | 0,3 |
| Compressive strength, MPa, not less than | 2,5 |
| Operating temperature, from...to, °C | +5 ... +30 |
It is used for high-quality plastering work on various mineral surfaces (concrete, brick) indoors and outdoors for plastering walls that are protected from moisture. Recommended for both mechanized and manual application. After hardening, it is a strong base for gypsum and lime putties and interior decorative plasters.
Thanks to the improved formula, the material provides:
• resistance to mold and fungi
• resistance to slipping due to good thixotropic properties
• machine and manual application
• high vapor permeability and crack resistance.
| Water consumption, per 30 kg of dry mix, l | 4,8...5,8 |
| Dry mix consumption per 1 mm of layer, kg/m², from | 1,3 |
| Estimated plaster layer thickness, mm, up to | 25 |
| Storage shelf life, h, not less than | 1 |
| Adhesion strength to the base in air-dry conditions, MPa, not less than | 0,3 |
| Compressive strength, MPa, not less than | 2,5 |
| Operating temperature, from...to, °C | +5 ... +30 |