It is used for high-quality plastering work on various mineral substrates (concrete, brick, aerated concrete, foam concrete). Recommended for plastering and repairing cracks, sinks, external walls and walls in rooms made of the above materials. After hardening, the plaster is a strong preparatory layer before applying putty or decorative plaster.
Thanks to the improved formula, the material provides:
• slip resistance due to good thixotropic properties;
• thermal insulation properties due to the use of perlite
• convenient application with the possibility of application by plastering machines;
• high vapor permeability and crack resistance.
| Mixing water proportions: - L / 1 kg - L / 25 kg |
0,22 - 0,26 5,5 - 6,0 |
| Dry mix consumption per 1 mm layer, kg/m², minimum | 1,2 |
| The estimated thickness of the plaster layer, mm | 5 ... 30 |
| The service life of the mortar mix, h, minimum | 1 |
| Vapor permeability, mg/(m∙h∙Pa), not less | 0,1 |
| Compressive strength limit, MPa, minimum | 5,0 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
It is used for high-quality plastering work on various mineral substrates (concrete, brick, aerated concrete, foam concrete). Recommended for plastering and repairing cracks, sinks, external walls and walls in rooms made of the above materials. After hardening, the plaster is a strong preparatory layer before applying putty or decorative plaster.
Thanks to the improved formula, the material provides:
• slip resistance due to good thixotropic properties;
• thermal insulation properties due to the use of perlite
• convenient application with the possibility of application by plastering machines;
• high vapor permeability and crack resistance.
| Mixing water proportions: - L / 1 kg - L / 25 kg |
0,22 - 0,26 5,5 - 6,0 |
| Dry mix consumption per 1 mm layer, kg/m², minimum | 1,2 |
| The estimated thickness of the plaster layer, mm | 5 ... 30 |
| The service life of the mortar mix, h, minimum | 1 |
| Vapor permeability, mg/(m∙h∙Pa), not less | 0,1 |
| Compressive strength limit, MPa, minimum | 5,0 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |