It is used for high-quality plastering work on various mineral surfaces (concrete, brick). Recommended for plastering external walls and walls in rooms with a wet operating mode. After hardening, the plaster is a strong preparatory layer before applying finishing putties, thin-layer decorative plasters, paints, tiling, etc.
| Water consumption per 25 kg of dry mix, l | 4.0...4.75 |
| Dry mix consumption per 1 mm layer, kg/m², minimum | 1,5 |
| Plastering area from 1 bag of 25 kg of dry mix (layer thickness 10 mm), m² | 1.7 |
| The estimated thickness of the plaster layer, mm | 10...20 |
| The service life of the mortar mix, h, minimum | 1 |
| Strength of adhesion to the base, MPa, minimum | 0,3 |
| Compressive strength limit, MPa, minimum | 7,5 |
| Frost resistance, cycle, not less than | 75 |
| Vapour permeability, not less than, mg/(m•h•Pa) | 0.07 |
| Operating temperature, ºС | -30...+70 |
It is used for high-quality plastering work on various mineral surfaces (concrete, brick). Recommended for plastering external walls and walls in rooms with a wet operating mode. After hardening, the plaster is a strong preparatory layer before applying finishing putties, thin-layer decorative plasters, paints, tiling, etc.
| Water consumption per 25 kg of dry mix, l | 4.0...4.75 |
| Dry mix consumption per 1 mm layer, kg/m², minimum | 1,5 |
| Plastering area from 1 bag of 25 kg of dry mix (layer thickness 10 mm), m² | 1.7 |
| The estimated thickness of the plaster layer, mm | 10...20 |
| The service life of the mortar mix, h, minimum | 1 |
| Strength of adhesion to the base, MPa, minimum | 0,3 |
| Compressive strength limit, MPa, minimum | 7,5 |
| Frost resistance, cycle, not less than | 75 |
| Vapour permeability, not less than, mg/(m•h•Pa) | 0.07 |
| Operating temperature, ºС | -30...+70 |