The mixture is used for rough levelling of the base (screed) for finishing coatings (self-levelling coatings – up to Grade 200, tiled coatings, etc.) after installation or during repair work both outside and inside the building. It can be used when installing heat-insulated flooring for filling heating elements (water heating element). *To save mortar and ensure protection against the occurrence of shrinkage cracks, in the screed with a thickness of more than 40 mm, it is recommended to add a large-sized (not more than half of the layer thickness) filling materials (expanded clay, granite crushed stone or solid bricks) in an amount not exceeding the initial volume of the mortar mix.
Mixing water proportions | 0,14 - 0,17 L / 1 kg 3,5 - 4,25 L / 25 kg |
Recommended thickness of the levelling layer, mm | 10 - 100* |
Consumption per 1 mm of the layer, kg/m² | 2,0 |
The service life of the mortar mix for laying, h | 1 |
The term of readiness of the levelling layer after laying, days - technological passage - laying of ceramic tiles - laying of other coatings |
1 3 7 |
Compressive strength at the age of 3/28 days, MPa, minimum | 5/20 |
The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
Shelf life, months | 12 |
The mixture is used for rough levelling of the base (screed) for finishing coatings (self-levelling coatings – up to Grade 200, tiled coatings, etc.) after installation or during repair work both outside and inside the building. It can be used when installing heat-insulated flooring for filling heating elements (water heating element). *To save mortar and ensure protection against the occurrence of shrinkage cracks, in the screed with a thickness of more than 40 mm, it is recommended to add a large-sized (not more than half of the layer thickness) filling materials (expanded clay, granite crushed stone or solid bricks) in an amount not exceeding the initial volume of the mortar mix.
Mixing water proportions | 0,14 - 0,17 L / 1 kg 3,5 - 4,25 L / 25 kg |
Recommended thickness of the levelling layer, mm | 10 - 100* |
Consumption per 1 mm of the layer, kg/m² | 2,0 |
The service life of the mortar mix for laying, h | 1 |
The term of readiness of the levelling layer after laying, days - technological passage - laying of ceramic tiles - laying of other coatings |
1 3 7 |
Compressive strength at the age of 3/28 days, MPa, minimum | 5/20 |
The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
Shelf life, months | 12 |