It is used for high-quality plastering work on various mineral surfaces (concrete, brick). Recommended for plastering external walls and walls in rooms with a wet operating mode. After hardening, the plaster is a strong preparatory layer before applying finishing putties, thin-layer decorative plasters, paints, tiling, etc.
| Water consumption per 25 kg of dry mix, l | 4,0...4,75 |
| Dry mix consumption per 1 mm of screed, kg/m², not less than | 1,5 |
| Plastering area from 1 bag of 25 kg of dry mix (layer thickness 10 mm), m² | 1,7 |
| Estimated thickness of plaster layer, mm | 10...20 |
| Potency time of mortar mixture, h, not less than | 1 |
| Adhesion strength to the base, MPa, not less than | 0,3 |
| Frost resistance, cycle, not less than | 75 |
| Compressive strength limit, MPa, not less than | 7,5 |
| Vapour permeability, not less than, mg/(m•h•Pa) | 0,07 |
| Operating temperature, ºС | -30...+70 |
It is used for high-quality plastering work on various mineral surfaces (concrete, brick). Recommended for plastering external walls and walls in rooms with a wet operating mode. After hardening, the plaster is a strong preparatory layer before applying finishing putties, thin-layer decorative plasters, paints, tiling, etc.
| Water consumption per 25 kg of dry mix, l | 4,0...4,75 |
| Dry mix consumption per 1 mm of screed, kg/m², not less than | 1,5 |
| Plastering area from 1 bag of 25 kg of dry mix (layer thickness 10 mm), m² | 1,7 |
| Estimated thickness of plaster layer, mm | 10...20 |
| Potency time of mortar mixture, h, not less than | 1 |
| Adhesion strength to the base, MPa, not less than | 0,3 |
| Frost resistance, cycle, not less than | 75 |
| Compressive strength limit, MPa, not less than | 7,5 |
| Vapour permeability, not less than, mg/(m•h•Pa) | 0,07 |
| Operating temperature, ºС | -30...+70 |