POLIMIN RX-2 FAST MIX MULTI is a fast-hardening polymer-cement mixture for anchoring elements of building structures and installing equipment, filling cavities in the base of foundations, installation gaps, and monolithic joints. The mixture allows filling cavities with a thickness of 20 mm to 50 mm. When filling cavities from 50 to 100 mm, up to 25% of washed crushed stone of a fraction of 5-10 mm by weight of the dry mixture should be added to the mortar mixture.
Thanks to the improved formula, the product provides:
• rapid strength development
• high adhesion to metal and concrete
• crack resistance
• water and frost resistance.
| Proportions of water for mixing, l, 1 kg/25kg | 0,08-0,12 / 2,0-3,0 |
| Mixture consumption per 1 liter of volume, kg | 2 |
| Application thickness, mm | 20...50 |
| Usage time, min, approx. | 60 |
| Bending tensile strength, MPa, not less than: 28 days | 7,5 |
| Compressive strength, MPa, not less than: 1 day 28 days |
40 60 |
| Bond strength to the base, MPa, not less | 1,5 |
| Frost resistance, cycle, not less | 50 |
| The temperature of the solution preparation, as well as the environmental conditions during operation, from ...to, ºС | +5 ...+30 |
| Operating temperature, from ...to, ºС | -50 ...+80 |
POLIMIN RX-2 FAST MIX MULTI is a fast-hardening polymer-cement mixture for anchoring elements of building structures and installing equipment, filling cavities in the base of foundations, installation gaps, and monolithic joints. The mixture allows filling cavities with a thickness of 20 mm to 50 mm. When filling cavities from 50 to 100 mm, up to 25% of washed crushed stone of a fraction of 5-10 mm by weight of the dry mixture should be added to the mortar mixture.
Thanks to the improved formula, the product provides:
• rapid strength development
• high adhesion to metal and concrete
• crack resistance
• water and frost resistance.
| Proportions of water for mixing, l, 1 kg/25kg | 0,08-0,12 / 2,0-3,0 |
| Mixture consumption per 1 liter of volume, kg | 2 |
| Application thickness, mm | 20...50 |
| Usage time, min, approx. | 60 |
| Bending tensile strength, MPa, not less than: 28 days | 7,5 |
| Compressive strength, MPa, not less than: 1 day 28 days |
40 60 |
| Bond strength to the base, MPa, not less | 1,5 |
| Frost resistance, cycle, not less | 50 |
| The temperature of the solution preparation, as well as the environmental conditions during operation, from ...to, ºС | +5 ...+30 |
| Operating temperature, from ...to, ºС | -50 ...+80 |