White cement-based adhesive mixture is intended for masonry and puttying* of external and internal walls made of precisely sized heat-insulating concrete (gas, foam concrete). The plasticity of the adhesive solution allows you to reduce the thickness of the joints to a minimum, which significantly reduces the likelihood of the formation of “cold bridges”. Due to its white color, it allows you to maintain the color uniformity of the walls without the use of additional decoration.
*Can be used for puttying the surfaces of the above-mentioned porous blocks using alkali-resistant fiberglass mesh, the layer thickness is not more than 10 mm.
| Water consumption per bag of 25 kg, l | 4.5-5.5 |
| Mixture consumption at a joint thickness of 3 mm, kg/m² | 6.0 - 7.0 |
| Estimated thickness of the masonry layer, from...to, mm | 2...10 |
| Consumption of the mix with a joint thickness of 3 mm, kg/m² | 6,0 - 7,0 |
| Masonry volume from a bag of 25 kg of dry mix at a block size of 600x400x288 and a joint thickness of 2 mm, m3 | 1.0 |
| Open time, min, not less than | 10 |
| Correction time, minutes, minimum | 5 |
| Suitability of the mortar mixture, h, not less than | 4 |
| Adhesion strength to the base, MPa, not less than | 0.3 |
| Compressive strength limit, MPa, not less than | 10.0 |
| Frost resistance, cycles, not less than | 50 |
| Base temperature, °C | +5...+30 |
White cement-based adhesive mixture is intended for masonry and puttying* of external and internal walls made of precisely sized heat-insulating concrete (gas, foam concrete). The plasticity of the adhesive solution allows you to reduce the thickness of the joints to a minimum, which significantly reduces the likelihood of the formation of “cold bridges”. Due to its white color, it allows you to maintain the color uniformity of the walls without the use of additional decoration.
*Can be used for puttying the surfaces of the above-mentioned porous blocks using alkali-resistant fiberglass mesh, the layer thickness is not more than 10 mm.
| Water consumption per bag of 25 kg, l | 4.5-5.5 |
| Mixture consumption at a joint thickness of 3 mm, kg/m² | 6.0 - 7.0 |
| Estimated thickness of the masonry layer, from...to, mm | 2...10 |
| Consumption of the mix with a joint thickness of 3 mm, kg/m² | 6,0 - 7,0 |
| Masonry volume from a bag of 25 kg of dry mix at a block size of 600x400x288 and a joint thickness of 2 mm, m3 | 1.0 |
| Open time, min, not less than | 10 |
| Correction time, minutes, minimum | 5 |
| Suitability of the mortar mixture, h, not less than | 4 |
| Adhesion strength to the base, MPa, not less than | 0.3 |
| Compressive strength limit, MPa, not less than | 10.0 |
| Frost resistance, cycles, not less than | 50 |
| Base temperature, °C | +5...+30 |