It is a mixture for masonry and puttying of external and internal walls from cellular concrete blocks (foam concrete, aerated concrete). The masonry mixture is used for the construction of walls from various masonry elements, mainly from aerated concrete, using thin-layer technology (seam width 3-5 mm). Types of permissible masonry elements: cellular concrete (aerated concrete), ceramic blocks, hollow bricks, lime-sand and other materials of this type.
| Composition: | cement, mineral fillers, functional additives |
| Color | gray |
| Mixing water proportions | 0,20 - 0,22 L / 1 kg 5,0 - 5,5 L / 25 kg |
| Consumption of the mix with a joint thickness of 3 mm, kg/m² | 6,0 - 7,0 |
| Suitability of the mortar mix, hours, minimum | 2 |
| Open time, minute, minimum | 10 |
| Correction time, minutes, minimum | 5 |
| Compressive strength limit, MPa, minimum | 5,0 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
| Shelf life, months | 12 |
It is a mixture for masonry and puttying of external and internal walls from cellular concrete blocks (foam concrete, aerated concrete). The masonry mixture is used for the construction of walls from various masonry elements, mainly from aerated concrete, using thin-layer technology (seam width 3-5 mm). Types of permissible masonry elements: cellular concrete (aerated concrete), ceramic blocks, hollow bricks, lime-sand and other materials of this type.
| Composition: | cement, mineral fillers, functional additives |
| Color | gray |
| Mixing water proportions | 0,20 - 0,22 L / 1 kg 5,0 - 5,5 L / 25 kg |
| Consumption of the mix with a joint thickness of 3 mm, kg/m² | 6,0 - 7,0 |
| Suitability of the mortar mix, hours, minimum | 2 |
| Open time, minute, minimum | 10 |
| Correction time, minutes, minimum | 5 |
| Compressive strength limit, MPa, minimum | 5,0 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
| Shelf life, months | 12 |