Polymer-mineral composition based on white cement with modifiers from leading European manufacturers and texture-forming grains.
The mixture is used for high-quality decorative decoration of building walls when performing both internal and external works. The texture can be created on various mineral surfaces: concrete, cement plasters (Polimip SHC-2, SHV-1), or used as one of the options for the final coating when insulating building facades using the POLIMIN THERMO FACADE system.
Thanks to the improved formula, the material provides:
• high vapor permeability
• protection of bonded thermal insulation systems
• plasticity when applying and forming the texture.
| Appearance of the finished coating | Textured aggregate plaster |
| Grain size Ø, mm | 1,5 / 1,8 |
| Mixing water proportions, L / 25 kg | 4,25 - 5,75 |
| Mixture consumption, kg/m², approx.:
grain Ø 1.5 mm grain Ø1.8 mm: |
2,4-2,6 2,7-3,2 |
| Strength of adhesion to the base, MPa, minimum | 0,5 |
| Vapour permeability, mg/(m·h·Pa), not less than | 0,1 |
| Frost resistance, cycles, not less than | 25 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
Polymer-mineral composition based on white cement with modifiers from leading European manufacturers and texture-forming grains.
The mixture is used for high-quality decorative decoration of building walls when performing both internal and external works. The texture can be created on various mineral surfaces: concrete, cement plasters (Polimip SHC-2, SHV-1), or used as one of the options for the final coating when insulating building facades using the POLIMIN THERMO FACADE system.
Thanks to the improved formula, the material provides:
• high vapor permeability
• protection of bonded thermal insulation systems
• plasticity when applying and forming the texture.
| Appearance of the finished coating | Textured aggregate plaster |
| Grain size Ø, mm | 1,5 / 1,8 |
| Mixing water proportions, L / 25 kg | 4,25 - 5,75 |
| Mixture consumption, kg/m², approx.:
grain Ø 1.5 mm grain Ø1.8 mm: |
2,4-2,6 2,7-3,2 |
| Strength of adhesion to the base, MPa, minimum | 0,5 |
| Vapour permeability, mg/(m·h·Pa), not less than | 0,1 |
| Frost resistance, cycles, not less than | 25 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |