One-component polyurethane foam with applicator, designed for professional installation, sealing and soundproofing. The product has high adhesion to most building materials, such as expanded polystyrene, PVC profiles, wood and wood-based materials, mineral surfaces (brick, concrete, plaster), metal. The foam does not stick to materials such as silicone, Teflon, polyethylene and polypropylene.
| Color | light yellow |
| Working temperature of the base, from ... to, °C | +5 ... +30 |
| Heat resistance (after curing), from ... to, °C | -50 ... +90 |
| Flammability | B3 (DIN 4102) |
| Time to disappear from sticking, min (20°C / rel. humidity 90%) | 6-12 |
| Time after which the cured foam can be cut, min | 45-55 |
| Time to complete curing, h | 24 |
| Maximum joint width, cm | 4 |
| Output from the cylinder, to, l (depending on the temperature and humidity of the environment) | 45 |
| Thermal conductivity, W/(m K) | 0,036 |
| Water absorption after 24 hours in water with partial immersion, kg/m2 | ≤1 |
| Solubility in organic solvents | acetone, before hardening |
| * All measurements were made under normal climatic conditions (+23°C+ 2°C, relative humidity 50 ±5%), unless otherwise stated. |
One-component polyurethane foam with applicator, designed for professional installation, sealing and soundproofing. The product has high adhesion to most building materials, such as expanded polystyrene, PVC profiles, wood and wood-based materials, mineral surfaces (brick, concrete, plaster), metal. The foam does not stick to materials such as silicone, Teflon, polyethylene and polypropylene.
| Color | light yellow |
| Working temperature of the base, from ... to, °C | +5 ... +30 |
| Heat resistance (after curing), from ... to, °C | -50 ... +90 |
| Flammability | B3 (DIN 4102) |
| Time to disappear from sticking, min (20°C / rel. humidity 90%) | 6-12 |
| Time after which the cured foam can be cut, min | 45-55 |
| Time to complete curing, h | 24 |
| Maximum joint width, cm | 4 |
| Output from the cylinder, to, l (depending on the temperature and humidity of the environment) | 45 |
| Thermal conductivity, W/(m K) | 0,036 |
| Water absorption after 24 hours in water with partial immersion, kg/m2 | ≤1 |
| Solubility in organic solvents | acetone, before hardening |
| * All measurements were made under normal climatic conditions (+23°C+ 2°C, relative humidity 50 ±5%), unless otherwise stated. |