The adhesive mixture is intended for laying ceramic and other facing materials with a water absorption of not less than 0.5%, with a size of not more than 400×400 mm on concrete, brick and plastered bases that do not deform, inside and outside the premises. When facing, it is recommended to use a two-sided (combined) method of applying the adhesive mixture. With the two-sided method, the adhesive solution is applied both to the base and to the back of the facing product, which increases the strength of the tile adhesion to the base. For gluing tiles with a water absorption of less than 0.5%, it is necessary to use the POLIMIN P-9 adhesive mixture with the addition of the POLIMIN RC-1 adhesive-elasticizing emulsion.
| Water consumption, per 25 kg of dry mix, l | 4.5...5.5 |
| Water consumption with the use of emulsion, l:
- water - emulsion |
2.5...3.5 2.0 5.0 |
| Consumption per 1 mm of layer, kg/m², from | 1.8 |
| Facing area from 1 bag of 25 kg of dry mix (layer thickness 2-3 mm), m² | 6.0 |
| Suitability of the mortar mix, h. not less than | 2 |
| Maximum thickness of the adhesive layer, mm | 10 |
| Open time, min, not less than | 20 |
| Readiness for jointing, days, not less than | 1 |
| Adhesion strength of ceramic tiles to a concrete base in air-dry conditions, at the age of 28 days, MPa, not less than | 0.6 |
| Frost resistance, cycles, not less than | 75 |
| Operating temperature, ºС, from...to | -30...+70 |
The adhesive mixture is intended for laying ceramic and other facing materials with a water absorption of not less than 0.5%, with a size of not more than 400×400 mm on concrete, brick and plastered bases that do not deform, inside and outside the premises. When facing, it is recommended to use a two-sided (combined) method of applying the adhesive mixture. With the two-sided method, the adhesive solution is applied both to the base and to the back of the facing product, which increases the strength of the tile adhesion to the base. For gluing tiles with a water absorption of less than 0.5%, it is necessary to use the POLIMIN P-9 adhesive mixture with the addition of the POLIMIN RC-1 adhesive-elasticizing emulsion.
| Water consumption, per 25 kg of dry mix, l | 4.5...5.5 |
| Water consumption with the use of emulsion, l:
- water - emulsion |
2.5...3.5 2.0 5.0 |
| Consumption per 1 mm of layer, kg/m², from | 1.8 |
| Facing area from 1 bag of 25 kg of dry mix (layer thickness 2-3 mm), m² | 6.0 |
| Suitability of the mortar mix, h. not less than | 2 |
| Maximum thickness of the adhesive layer, mm | 10 |
| Open time, min, not less than | 20 |
| Readiness for jointing, days, not less than | 1 |
| Adhesion strength of ceramic tiles to a concrete base in air-dry conditions, at the age of 28 days, MPa, not less than | 0.6 |
| Frost resistance, cycles, not less than | 75 |
| Operating temperature, ºС, from...to | -30...+70 |