It is used for performing mechanized (using plastering stations) and manual, high-quality plastering works, on various mineral bases. It is recommended for plastering surfaces in rooms with dry operation. After finishing smoothing, it gives a smooth surface, which, as a rule, does not require puttying. Thanks to perlite, the mixture has improved heat, sound insulation and fire protection properties. Do not use in direct contact with iron.
| Color | light |
| Water consumption l/h, from (water consumption depends on the type of plastering station) | 700 |
| Dry mix consumption per 10 mm layer, kg/m², not less than | 8,5 |
| Layer thickness per pass, from...to, mm | 5...30 |
| Maximum operational thickness, mm, wall | 60 |
| Maximum operational thickness, mm, ceiling | 15 |
| Fire safety, CLASS | A1 |
| Start of hardening, min | ≥ 50 |
| Storage shelf life, h, not less than | 1 |
| Bending tensile strength, H/mm² | ≥ 1,0 |
| Compressive strength, H/mm² | ≥ 2,0 |
| Mixture preparation temperature and base temperature, from...to, °С | +5 ºС ...+30 |
It is used for performing mechanized (using plastering stations) and manual, high-quality plastering works, on various mineral bases. It is recommended for plastering surfaces in rooms with dry operation. After finishing smoothing, it gives a smooth surface, which, as a rule, does not require puttying. Thanks to perlite, the mixture has improved heat, sound insulation and fire protection properties. Do not use in direct contact with iron.
| Color | light |
| Water consumption l/h, from (water consumption depends on the type of plastering station) | 700 |
| Dry mix consumption per 10 mm layer, kg/m², not less than | 8,5 |
| Layer thickness per pass, from...to, mm | 5...30 |
| Maximum operational thickness, mm, wall | 60 |
| Maximum operational thickness, mm, ceiling | 15 |
| Fire safety, CLASS | A1 |
| Start of hardening, min | ≥ 50 |
| Storage shelf life, h, not less than | 1 |
| Bending tensile strength, H/mm² | ≥ 1,0 |
| Compressive strength, H/mm² | ≥ 2,0 |
| Mixture preparation temperature and base temperature, from...to, °С | +5 ºС ...+30 |