It is used to obtain masonry and plaster mortars of high strength (Grade 100) for both indoor and outdoor works.
| Composition: | cement, mineral fillers, functional additives |
| Mixing water proportions | 0,16 - 0,18 L / 1 kg 4,0 - 4,5 L / 25 kg |
| Consumption per 1 mm of the layer, kg/m² | 1,6 |
| The estimated thickness of the plaster/masonry layer, mm | 10 - 20 / 5 - 10 |
| Suitability of the mortar mix, hours | minimum 2 |
| Compressive strength, at the age of 28 days, MPa | minimum 10,0 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
| Shelf life, months | 12 |
It is used to obtain masonry and plaster mortars of high strength (Grade 100) for both indoor and outdoor works.
| Composition: | cement, mineral fillers, functional additives |
| Mixing water proportions | 0,16 - 0,18 L / 1 kg 4,0 - 4,5 L / 25 kg |
| Consumption per 1 mm of the layer, kg/m² | 1,6 |
| The estimated thickness of the plaster/masonry layer, mm | 10 - 20 / 5 - 10 |
| Suitability of the mortar mix, hours | minimum 2 |
| Compressive strength, at the age of 28 days, MPa | minimum 10,0 |
| The temperature of the base and ambient temperature during application, °С | +5 ... +30 |
| Shelf life, months | 12 |