One-component waterproofing mastic POLIMINСGl-10 for creating a continuous seamless coating waterproofing of walls and floors in rooms operated in wet conditions (bathrooms, showers, toilets and other public and industrial facilities) with subsequent surface cladding. Effective as an adhesive for Polimiп GL-2 waterproofing tapes. Can be used in underfloor heating systems. Do not use as a finishing coating. For sealing swimming pools and building structures operated under constant water exposure, it is necessary to use other Polimin materials of the GI group.
| Color | blue |
| Density, g/cm³ | 1.4 |
| Drying time of the 1st layer, not less than, h | 2 |
| Drying time of the 2nd layer, not less than, h | 6 |
| Consumption, kg/m² from | 1.0 |
| Expiration before facing works, hours | 24 |
| Consumption at a layer thickness of 1 mm, from, kg/m² | 0.9 |
| Consumption for 2 layers, from, kg/m² | 1.2 |
| Water permeability | absent |
| Ability to bridge cracks at +20 °C, mm | > 1.0 |
| Initial bond strength, after heat and water exposure, N/mm² | > 0.5 |
| Declaration of properties | CPR 20/047 |
One-component waterproofing mastic POLIMINСGl-10 for creating a continuous seamless coating waterproofing of walls and floors in rooms operated in wet conditions (bathrooms, showers, toilets and other public and industrial facilities) with subsequent surface cladding. Effective as an adhesive for Polimiп GL-2 waterproofing tapes. Can be used in underfloor heating systems. Do not use as a finishing coating. For sealing swimming pools and building structures operated under constant water exposure, it is necessary to use other Polimin materials of the GI group.
| Color | blue |
| Density, g/cm³ | 1.4 |
| Drying time of the 1st layer, not less than, h | 2 |
| Drying time of the 2nd layer, not less than, h | 6 |
| Consumption, kg/m² from | 1.0 |
| Expiration before facing works, hours | 24 |
| Consumption at a layer thickness of 1 mm, from, kg/m² | 0.9 |
| Consumption for 2 layers, from, kg/m² | 1.2 |
| Water permeability | absent |
| Ability to bridge cracks at +20 °C, mm | > 1.0 |
| Initial bond strength, after heat and water exposure, N/mm² | > 0.5 |
| Declaration of properties | CPR 20/047 |