SHC5_LShC-5 START-FINISH HEAT PRESERVING PLASTER FOR GAS CONCRETE

  • INTERIOR AND EXTERIOR WORKS
  • MANUAL AND MACHINE APPLICATION
  • WATER REPELLING EFFECT
  • HIGH PLASTICITY
  • CONTAINS PEARLITE

COMPOSITION AND APPLICATION

Polymineral composition on the basis of cement with pearlite and modifiers of leading European manufacturers that facilitate enhancement of mechanical properties of solution and its adhesion.

Plaster is used for high quality plaster works on different mineral bases (concrete, bricks, aerated concrete, foam concrete). Recommended for plastering and repair cracks, sinks, outside walls and walls in premises manufactured of abovementioned materials. After solidification it becomes strong preparation layer for application of cement putty or decorative plaster.

SPECIFICATIONS

  • Water requirement for 25 kg of dry mix, l – 5.5…6.5
  • Dry mix consumption for 1 mm layer, kg/m2, starting from  – 1.3
  • *Plastering area of 1 bag (25 kg) of dry mix, (layer thickness 5 mm), m2  – 4.0
  • Plaster layer thickness, from…to, mm – 5…30
  • Applicability of solution mix, hours, not less – 1
  • Strength of adhesion with base under dry air conditions, MPa, not less – 0.3
  • Compression strength limit, MPa, not less – 5.0
  • Freeze resistance, cycles – 50
  • Operational temperature, °С  –  -30…+70

Average consumption: bag 25 kg for 2 m2